| Property | Unit |
Test Method |
Test Condition |
Result |
| Melt Flow Index |
g/10 min | ASTM D-1238 |
230℃×2.16Kg | 8 |
| Tensile Strength at Yield |
MPa | ASTM D-638 |
23℃ | 34 |
| Tensile Elongation at Break |
ASTM D-638 |
23℃ | 100 | |
| Flexural Modulus |
MPa | ASTM D-790 |
23℃ | 1570 |
| Flexural
Strength |
MPa | ASTM D-790 |
23℃ | 46 |
| Izod Impact Strength |
ft-lb/in | ASTM D-256 |
23℃ |
1.69 |
| Heat Deflection Temperature |
℃ | ASTM D-648 |
0.46MPa | 130 |
| Specific Gravity | g/cm3 | ASTM D-792 |
23℃/23℃ | 0.940 |
| Fire Retardance | UL 94 | 1.5mm | V-2 |
PP MI35
| Density
(g/cm3) |
MFR
(Melt Flow Rate) (g/10min) |
Shrinking Percentage (%) | Rockwell
Hardness (R scale) |
Coefficient
of Stiffness (kg/cm 2) |
IZOD Notch Impact Strength (kg.cm/cm) | HDT(Heat Deflection Temperature)
(℃) |
Softening Temperature
(℃) |
| 0.90 | 35 | 1.3-1.7 | 100 | 10000 | 23℃ 8.5
-20℃ 2.5 |
105 | 140 |
PP V30G1
Property |
Unit |
Result |
| Melt Flow Index |
g/10 min | 16±3.0 |
| Tensile Strength at Yield |
MPa | ≥33 |
| Rockwell hardness | R-Scale | ≥85 |
| Flexural Modulus |
MPa | ≥1350 |
| Izod Impact Strength |
J/m | 29 |
| Heat Deflection Temperature |
℃ | ≥85 |
| Ash Content | % | ≤0.02 |
| Cleanness | ≤10 |
PP S7OO
| properties project | Test condition | Nominal Value Unit | |
| properties | Melt Mass-Flow Rate (MFR) | 230℃,2.16kg | 12-18g/10min |
| mechanical | Tension yield strength | ≥32.0 MPa | |
| Other properties | isotacticity index | ≥96.0% | |
| color chip | ≤5/kg | ||
| Powder ash | ≤0.01%(m/m) | ||
| fisheye | 0.8mm | ≤3 /1520cm2 | |
| fisheye | 0.4mm | ≤10 /1520cm2 | |